Selective absorbing glass
POSITION >>
HOME
>
Selective absorbing glass
>
Red glass |
Model
| Thickness | A[2856k] | D65 | Chemical Stability | ND | α×10-7 | Tg | Ts | S | (mm) | x | y | Y | x | y | Y | DA | DW | (/℃) | (℃) | (℃) | HB1 | 2 | 0.457 | 0.403 | 74.4 | 0.319 | 0.325 | 73.2 | | | 1.673 | | | | 4.09 | HB3 | 2 | 0.642 | 0.337 | 16.6 | 0.578 | 0.324 | 11.1 | | | 1.604 | 102 | 577 | 638 | 3.37 | HB5 | 2 | 0.401 | 0.133 | 0.2 | 0.204 | 0.039 | 0.2 | 2 | 2 | 1.591 | | | | 3.26 | HB6 | 2 | 0.569 | 0.365 | 1.4 | 0.403 | 0.251 | 1 | 3 | 3 | | | | | |
Model | Thickness | 405 (nm) | 420 (nm) | 436 (nm) | 510 (nm) | 530 (nm) | 570 (nm) | 650 (nm) | 680 (nm) | 700 (nm) | Bubbles | Stripe | Stress | (mm) | *HB1 | 2 | | 74.3~80.7 | | 57.9~71.3 | | 63.5~74.7 | | ≥76.4 | | C | 3C | 3 | HB3 | 2 | | | 1.0-9.0 @440 | | ≤0.9 | | 45.0~70.0 | | | C | 3C | 3 | *HB5 | 2 | ≥35.7 | | ≤7.1 | | | | | | | C | 4 | 3 | HB6 | 2 | | | | | | 0.8-2.0 @ 590 | 1.1-2.5 @ 640 | | 2.1~4.8 | C | 4 | 3 |
|